Modification and characterization of the surface of AISI 8620 steel by C-TIGA and P-TIGA processes in one pass
This research investigates the effects of continuous tungsten inert gas arcing (C-TIGA) and
pulsed tungsten inert gas arcing (P-TIGA) processes on the hardness of case-hardenable …
pulsed tungsten inert gas arcing (P-TIGA) processes on the hardness of case-hardenable …
Increasing the wear resistance of gears during laser hardening
V Biryukov - E3S Web of Conferences, 2024 - e3s-conferences.org
The paper presents the main results of metallographic studies and tribotechnical tests of
steel for the production of 25CrMnTi gears. Quenching of the samples was performed using …
steel for the production of 25CrMnTi gears. Quenching of the samples was performed using …
Aynı Sıcaklıkta Uygulanan Isıl İşlem ve Farklı Oranda Uygulanan Redüksiyon İşleminin Fren Borularına Mekanik Özelliklerine Etkisinin Araştırılması
Bu çalışmada, 3, 40 mm ve 4, 75 mm dış çapa sahip fren borularına 3, 20 mm ve 4, 65 mm
dış çapa sahip olacak şekilde redüksiyon işlemi uygulanmıştır. Ardından fren borularına …
dış çapa sahip olacak şekilde redüksiyon işlemi uygulanmıştır. Ardından fren borularına …