Insights into the adsorption and interfacial products improving the wetting of the Ag-Ti/graphite and Cu-Ti/graphite systems: a first-principles calculation
Introducing actives into brazing alloys is a common way to improve their wettability. Typical
interfacial behaviors of added actives involve adsorbing at the liquid/solid interface and …
interfacial behaviors of added actives involve adsorbing at the liquid/solid interface and …
Low temperature brazing between pre-metallized ZrO2 ceramics and medical pure titanium using AuSn20 filler metal
N Jiang, H Bian, J Li, X Song, Y Lei, W Long, H Niu… - Vacuum, 2022 - Elsevier
ZrO 2 ceramic was metallized by Sn-xTi (x= 2, 3 and 4 at.%) foils at 1000° C for 30 min. As
the Ti content was 3%, the continuous and homogeneously distributed Ti–O compounds …
the Ti content was 3%, the continuous and homogeneously distributed Ti–O compounds …
Induction brazing of Al2O3 ceramic and 316L stainless steel with Sn–Ti filler alloy
An induction brazing method for joining Al 2 O 3 ceramic to 316L stainless steel (SS) was
developed in this study. The Sn–Ti alloy was rapidly melted by induction heating, which …
developed in this study. The Sn–Ti alloy was rapidly melted by induction heating, which …
Reactive wetting and interfacial characterization of ZrO2 by SnAgCu-Ti alloy
The reactive wetting behavior of zirconia with SnAgCu-x% Ti (SAC-x% Ti, wt%, x= 1, 4) alloy
was investigated via the sessile drop method in isothermal experiments. As temperatures …
was investigated via the sessile drop method in isothermal experiments. As temperatures …
Insight into the wetting behavior and interfacial evolution of Sn-xZr/ZrO2 systems at 850-950℃
The wetting behavior of the Sn-Zr/ZrO 2 system was investigated by different drop methods,
and the influencing of temperature and Zr content on the wetting interfacial microstructure …
and the influencing of temperature and Zr content on the wetting interfacial microstructure …
Wettability and joining of SiC by Sn-Ti: Microstructure and mechanical properties
Abstract Reliable SiC/Sn-Ti/SiC joints were obtained by brazing (950° C/10 min) and
soldering (250° C/2 min) following premetallization depend on the wettability of Sn-Ti on …
soldering (250° C/2 min) following premetallization depend on the wettability of Sn-Ti on …
Wetting of AlN by moten Cu-8.6 Zr-xTi ternary alloys at 1373 K
Q Lin, L Wang, R Sui - Acta Materialia, 2021 - Elsevier
The wetting of AlN by molten Cu-8.6 Zr-xTi (x= 0, 5, 7.5, and 10 at.%) ternary alloys was
conducted by the modified sessile drop method at 1373 K under a high vacuum. AlN cannot …
conducted by the modified sessile drop method at 1373 K under a high vacuum. AlN cannot …
Interactions, joining and microstructure of Sn-Ti/ZrO2 system
Brazing and soldering following pre-metallization were employed to obtain reliable ZrO 2/Sn-
Ti/ZrO 2 joints. Both the metallization and brazing depend on the wettability of ZrO 2 by Sn-Ti …
Ti/ZrO 2 joints. Both the metallization and brazing depend on the wettability of ZrO 2 by Sn-Ti …
Wetting behavior of Al on the surface of SiC textured by nanosecond laser
Z Fan, J Zhao, J Yin, D Hu, W Fu, H Yan… - Optics & Laser …, 2022 - Elsevier
Recently ultrafast laser has been used to process materials to obtain functional surface.
However, most of the existing research is focused on metals, and only a few studies …
However, most of the existing research is focused on metals, and only a few studies …
Low temperature brazing of biomedical titanium and zirconia metallized with Sn-Ti metal foil
YZ Lei, H Bian, N Jang, XG Song, JC Li, HY Zhao… - Materials …, 2022 - Elsevier
Zirconia ceramic and titanium have been applied more and more extensively in biomedical
fields. In this work, reliable brazed joints of ZrO 2/Sn-3Ti/AuSn20/Ti were achieved by pre …
fields. In this work, reliable brazed joints of ZrO 2/Sn-3Ti/AuSn20/Ti were achieved by pre …