Enhanced critical current density in Gd-added (Bi, Pb)-2212 bulk superconductor
A Biju, RP Aloysius… - … Science and Technology, 2005 - iopscience.iop.org
The effects of Gd addition on the phase evolution and superconducting properties of (Bi, Pb)-
2212 prepared in the bulk polycrystalline form were studied. The Gd content in the samples …
2212 prepared in the bulk polycrystalline form were studied. The Gd content in the samples …
Yttrium cuprates modification in linear generator application for power generation
ME Emetere - Clean Energy, 2024 - academic.oup.com
Yttrium barium copper oxide (YBCO) is used for special applications in linear generators
because of its excitation loss, lower weight, and higher efficiency. These qualities enable the …
because of its excitation loss, lower weight, and higher efficiency. These qualities enable the …
Superconductivity and flux pinning in Dy added (Bi, Pb)-2212 superconductor
A Biju, PM Sarun, RP Aloysius… - Superconductor …, 2006 - iopscience.iop.org
The changes in phase evolution, structural, superconducting and flux pinning properties of
(Bi, Pb)-2212 superconductor due to the addition of the rare earth Dy have been studied …
(Bi, Pb)-2212 superconductor due to the addition of the rare earth Dy have been studied …
Sintering effects in Na-substituted Bi-(2212) superconductor prepared by a polymer method
M Gürsul, A Ekicibil, B Özçelik, MA Madre… - … of Superconductivity and …, 2015 - Springer
In this study, Na-substituted Bi 2 Sr 2 Ca 0.9 Na 0.1 Cu 2 O superconductor samples were
prepared by a polymer solution method. Three different sintering temperatures (850, 860 …
prepared by a polymer solution method. Three different sintering temperatures (850, 860 …
Magnetic alignment in 2212 Bi-based superconducting system: Part I. Magnetic orientation of Bi2Sr2Ca1− x (RE) xCu2O8− y [(RE)= Gd, Dy, Ho, Er] powder dispersed …
S Stassen, R Cloots, P Vanderbemden… - Journal of materials …, 1996 - cambridge.org
The magnetic anisotropy of rare-earth substituted 2212 materials (Bi2Sr2Ca0. 8RE0.
2Cu2Ox with RE= Gd, Dy, Ho, Er) is put into evidence. Superconducting powder dispersed …
2Cu2Ox with RE= Gd, Dy, Ho, Er) is put into evidence. Superconducting powder dispersed …
Magnetic alignment in 2212 Bi-based superconducting system: II. Bi2Sr2Ca1−xDyxCu2O8−yx = 0.2 glass recrystallized in 0.6 T magnetic field
Starting from a glassy precursor, Bi 2 Sr 2 Ca 1− x Dy x Cu 2 O 8− y (for x= 0.2) was
recrystallized under a 0.6 T magnetic field. After splat quenching, the samples were heated …
recrystallized under a 0.6 T magnetic field. After splat quenching, the samples were heated …
Phase Relations in the Bi–Sr–Ca–Cu–M–O (M= Y, Dy, Ho, Er, Tm, Yb, Lu) Systems
PE Kazin, DD Zaitsev, YD Tret'yakov, M Jansen - Inorganic materials, 2001 - Springer
The phase relations in the Bi–Sr–Ca–Cu–M–O (M= Y, Dy, Ho, Er, Tm, Yb, Lu) systems near
Bi 2 Sr 2 CaCu 2 O 8+ x (Bi-2212) were studied between 850 and 990° C. The results …
Bi 2 Sr 2 CaCu 2 O 8+ x (Bi-2212) were studied between 850 and 990° C. The results …
Magnetic texturing of bulk samples of the superconductor Bi2Sr2Ca0. 8Dy0. 2Cu2O8-y
S Stassen, A Rulmont, P Vanderbemden… - Journal of applied …, 1996 - orbi.uliege.be
The texturing process of Bi-Sr-Ca (Dy)-Cu-O (2212) is optimized by sintering under a
magnetic field. The precursor crystalline powder is melted and grown under a 1.2 T …
magnetic field. The precursor crystalline powder is melted and grown under a 1.2 T …
[引用][C] Doping of a Bi2Sr2Cu2O8 + x -Based Superconducting Material with Lanthanide- and Scandium-Containing Oxides
PE Kazin, DD Zaitsev, YD Tret'yakov - Doklady Chemistry, 2002 - Springer
The reaction of Bi-2212 with heavier lanthanides with smaller ionic radii results in the
formation of two phases enriched in Ln: copper-free double perovskite and cuprate …
formation of two phases enriched in Ln: copper-free double perovskite and cuprate …