The microstructures of the reaction interfaces between slag and corundum aggregates,
microporous corundum produced in the laboratory and tabular corundum were observed …

Highly corrosion resistant Cr 2 O 3 based refractory linings are required for waste melting
furnaces due to the complex melting environment. However, these linings are susceptible to …

Corroded microstructure of a Cr 2 O 3-Al 2 O 3-ZrO 2 refractory brick after 4200 h service in a
gasifier was investigated. An isolation layer comprising mainly (Mg, Fe 2+)(Cr, Fe) 2 O 4 …

Hot corrosion behavior of Al 2 O 3–Cr 2 O 3 refractory by molten glass at 1200° C under
static condition was monitored. Glass-refractory interface was investigated by XRD, SEM …

Four chromium oxide-free refractories based on spinel, alumina, and calcium aluminates are
brought in contact with three ashes from coal and biomass with different base to acid ratios …

Durability and corrosion behavior of refractory lining, a core part of a commercial water‐coal
slurry gasifier, largely determine its gas yield rate and carbon conversion rate. In this work …

Recently, a new high-temperature ternary Cr (III) phase (Wuboraite, CaAl 2 Cr 2 III O 7) was
synthesized in the Al 2 O 3–CaO–Cr 2 O 3 system. However, its formation & chemical …

Periodical relining of the gasifier due to refractory corrosion and failure is a major cost driver
in the coal gasification industry. In the present work, the failure mechanisms of Cr 2 O 3-Al 2 …

This study investigated the degradation mechanisms of SiC-MgAl 2 O 4 refractory materials
in a bench-scale entrained flow gasifier. Layered degradation and protective SiO 2 formation …

As a crucial component of an opposed multi-burner (OMB) coal-water slurry gasifier, severe
degradation of the refractory lining frequently results in costly operation delays. In this work …