Industrial atmospheric corrosion resistance of P-RE weathering steel
F Mi, X Wang, Z Liu, B Wang, Y Peng, D Tao - Journal of Iron and Steel …, 2011 - Springer
The corrosion behavior of low-carbon steel (CS), P-bearing steel (PS) and P-RE weathering
steel (P-REWS) exposed for two years in Jiangjin of China was investigated. The results …
steel (P-REWS) exposed for two years in Jiangjin of China was investigated. The results …
Corrosion behavior of S450EW low-alloy weathering steel in cyclically alternate corrosion environments
J Wang, P Shi, C Liu, M Jiang - Journal of Iron and Steel Research …, 2015 - Springer
Weathering steel is widely used in various fields due to its excellent mechanical properties
and high corrosion resistance. The effect of chromium content on the S450EW weathering …
and high corrosion resistance. The effect of chromium content on the S450EW weathering …
闪速燃烧合成的Fe-Si3N4中FexSi粒子的形成机理
陈俊红， 宋文， 刘晓光， 孙加林 - 工程科学学报, 2009 - cje.ustb.edu.cn
采用SEM, EDS 等手段研究了闪速燃烧合成的氮化硅铁及其原料FeSi75 的组成, 结构,
并结合闪速燃烧合成工艺和热力学分析, 揭示氮化硅铁中Fe x Si 粒子的形成机理. 结果表明 …
并结合闪速燃烧合成工艺和热力学分析, 揭示氮化硅铁中Fe x Si 粒子的形成机理. 结果表明 …
Cu-P-RE 耐候钢的耐蚀性能
岳丽杰， 陈为公， 王龙妹 - 工程科学学报, 2009 - cje.ustb.edu.cn
通过干湿周浸加速腐蚀实验研究了不同稀土含量的耐候钢和对比普碳钢的腐蚀行为及其耐蚀
性能. 采用失重法测得了各试样的腐蚀率; 结果发现, 稀土耐候钢的腐蚀率远远低于普碳钢的 …
性能. 采用失重法测得了各试样的腐蚀率; 结果发现, 稀土耐候钢的腐蚀率远远低于普碳钢的 …
Formation mechanism of Fe_xSi particles in ferro-silicon nitride prepared via flashing combustion
J CHEN, W SONG, X LIU, J SUN - Chinese Journal of Engineering, 2009 - cje.ustb.edu.cn
The composition and structure of ferro-silicon nitride prepared via flashing combustion and
the starting material FeSi75 were analyzed by SEM and EDS. The formation mechanism of …
the starting material FeSi75 were analyzed by SEM and EDS. The formation mechanism of …
Corrosion Resistance Properties of a Nickel–Chromium Steel Bar in Marine Atmosphere
B Wu, Y Qi, H Zhou, Z Zou - Metallurgist, 2020 - Springer
The corrosion behaviors of Ni–Cr and 20MnSi steel bars in a simulated marine atmosphere
are compared using alternate immersion corrosion tests and electrochemical techniques …
are compared using alternate immersion corrosion tests and electrochemical techniques …
Corrosion resistance of Cu-P-RE weathering steel
L YUE, W CHEN, L WANG - Chinese Journal of Engineering, 2009 - cje.ustb.edu.cn
The corrosion behavior and corrosion resistance of Cu-P-RE weathering steel and plain
carbon steel were studied by drywet cycle immersion test. A weight-loss method was used to …
carbon steel were studied by drywet cycle immersion test. A weight-loss method was used to …
Effect of rare elements on corrosion behavior of SPCC in CSP
YF Zhou, WJ Qiu, WX Li, J Xie - Advanced Materials Research, 2013 - Trans Tech Publ
The corrosion process of rare earth (RE) SPCC steel and SPCC steel in CSP in 3.5% NaCl
solutions was investigated by SEM, EDS, XRD and polarization curve measurements. The …
solutions was investigated by SEM, EDS, XRD and polarization curve measurements. The …
Research of the Pits Induced by MnS Inclusions at the Incipient Stage of Cavitation Erosion
J Nana, L Shihan, C Haosheng, W Jiadao… - … Tribology: Proceedings of …, 2010 - Springer
The pits formed at the incipient stage of cavitation erosion of 45 steel have been investigated
by using a standardized vibration cavitation apparatus with de-ionized water. Scanning …
by using a standardized vibration cavitation apparatus with de-ionized water. Scanning …