The oxidation behavior of a martensitic stainless steel with or without glass coating was
investigated at 600–800° C. The glass coating provided effective protection for the stainless …

Surface oxidation of the duplex stainless steel DSS alloy 2205 was studied by X-ray
photoelectron spectroscopy (XPS) and SEM imaging. The experiments were performed on …

Thermal fatigue tests were conducted on a high Si low Mo ductile cast iron (DCI) under
oxidation conditions at 600° C. The study aimed to understand the evolution of surface …

The isothermal oxidation behaviors of the Fe-25Cr-20Ni-χNb (0–1.6 wt.%) weld metals have
been investigated in air at 1100° C. Results showed that niobium has a detrimental effect on …

This study elucidates the impact of the microstructure of Fe-16Cr-0.2 C on oxide layer
formation at 650° C in Ar-0.5% SO 2. A cold-rolled and two heat-treated states of the alloy …

High-temperature oxidation of duplex stainless steels S32101 and S32304 was performed
under three conditions: isothermal oxidation at 1050° C in air and simulated industrial …

High-temperature oxidation behavior and the mechanism of hyper duplex stainless steel
S32707 were investigated at 900, 1000, 1100 and 1200° C in air. Some interesting oxidation …

This study focuses on the characterization of the oxide scales formed after different exposure
times in the range of 2.5–20 min. A commercially available ferritic steel grade AISI 441 was …

Duplex stainless steel exhibits a dual phase microstructure of austenite islands in a ferrite
matrix. The oxidation characteristics of the phases depend on the composition within them …

Abstract Effect of Mn on microstructure, mechanical property and pitting corrosion of 19% Cr
economical duplex stainless steels with solution temperatures ranging from 1040 to1220° C …