T Carisey, I Leviri, DG Brandon - Journal of the European Ceramic Society, 1995 - Elsevier
The mechanical properties of a highly textured alumina have been studied and show a significant improvement in bend strength and Weibull modulus when compared to a …
Использование бадделеита особенно важно в рамках программы импортозамещения и повышения конкурентоспособности отечественной продукции. В книге обобщены …
SG Huang, K Vanmeensel, O Van der Biest… - Journal of the European …, 2007 - Elsevier
ZrO2–WC ceramic composites with 40vol% WC were consolidated by pulsed electric current sintering (PECS) for 4min at 1450° C under a pressure of 60MPa. The effect of ZrO2 …
M Poorteman, M Traianidis, G Bister… - Journal of the European …, 2009 - Elsevier
Multiwall Carbon Nanotubes (MWCNT)-alumina nanocomposites have been fabricated by colloidal processing and uniaxial hot pressing. In the nanotube sols, the electrical …
Z Pędzich, K Haberko, J Piekarczyk, M Faryna… - Materials Letters, 1998 - Elsevier
Zirconia matrix composites with tungsten carbide inclusions were obtained by hot pressing at 1400° C for 40 min. The carbide particle content was changed from 10 to 50 vol.%. All the …
AS Sokolov, VG Harris - Journal of the European Ceramic Society, 2018 - Elsevier
Non-cubic crystals exhibit anisotropic physical and functional properties. Microscopic crystallites as constituents of polycrystalline materials are randomly oriented, thus …
This work adds new experimental facts on room temperature hardness and flexural strength of alumina and composites with 1, 2, 5 and 10 vol% single-walled carbon nanotubes …
K Haberko, W Pyda, Z Pȩdzich, MM Bućko - Journal of the European …, 2000 - Elsevier
A TiO2–Y2O3–ZrO2 solid solution was prepared by the coprecipitation–calcination technique. The resulting powder of+ 100 m2/g specific surface area was mixed with a …
A Selcuk, C Leach, RD Rawlings - Journal of the European Ceramic …, 1995 - Elsevier
A study has been carried out on the processing of silicon carbide platelet-reinforced yttria- stabilised zirconia ceramics, using slip casting techniques followed by cold isostatic …